Behaviour of copper and nickel during high temperature oxidation of steel containing them... It is well known that copper causes hot shortness problem and nickel suppresses the effect of copper....
Aisi/doe technology roadmap program: effects of residuals in carbon steels... The influence of residuals (Cu, Sn, Ni, P, Si, up to the levels studied here), on these laboratory produced hot rolled steels was studied in the areas of (a) hot ductility, (b) surface hot shortness, (c) scale formation and adherence, and (d) embrittlement and mechanical properties....
The effect of copper on hot shortness of low carbon aluminium killed steel in thin slab casting / sabrudin mohamad surenThe surface hot shortness phenomenon causes cracks with high degree of difficulty to be eliminated during subsequent processing resulting surface defects especially in hot rolled coils and...
Review of hot shortness problems in copper-containing steelaudience: researcher, professional, studentThe problem of hot shortness is first briefly discussed in terms of the recycling of scraps and the occurrence of various residual elements in steel....