Time-dependent crack growth mechanisms in alloy 617 at 800°c in air... Fracture surfaces and crack tip profiles were examined to discover relevant relationships between transgranular cracking, void growth and coalescence, and the role of oxygen embrittlement....
Stress corrosion cracking of nickel base superalloys in aerated supercritical water... in a temperature domain where nickel base superalloys exhibit oxygen embrittlement....
Reply to comment on “identification of sagbo-induced damage zone ahead of crack tip to characterize sustained loading crack growth in alloy 783”The damage zone, formed during sustained loading by stress accelerated grain boundary oxygen embrittlement, is a localized region ahead of the crack tip....
A damage mechanics model for creep and oxygen embrittlement in metals... Then, using the creep damage mechanics model as a foundation, a framework is presented for treating the phenomenon of stress-accelerated grain-boundary oxygen embrittlement (SAGBO) in metals (e.g....